What is 6061-T6 aluminum used for?

Contents

What is 6061-T6 aluminum used for?

6061 Aluminum Sheet The T6 refers to the temper or degree of hardness, which is achieved by precipitation hardening. This grade has a good strength-to-weight ratio and is also heat-treatable. With great formability and weldability, it is used for engineering and structural applications, boats, furniture, and more.

Is there a difference between 6061 and 6061-T6?

Generally, 6061 aluminum is solution heat treated, then aged. T4 temper aluminum is naturally aged, and T6 temper aluminum is artificially aged for maximum strength.

Is 6061-T6 heat treated?

Aluminium / Aluminum 6061 alloy is heat-treated at 533°C (990°F) for a sufficient period of time followed by quenching in water. The precipitation hardening process can be performed at 160°C (320°F) for 18 h followed by air cooling. This process is again repeated at 177°C (350°F) for 8 h followed by cooling in air.

Is 6061-T6 machinable?

Did you know? Aluminium 6061-T6 is a sub-category of the 6061 alloy, one of the most widely used aluminium alloys. Compared to other Aluminium 6061 variations, 6061-T6 has better machinability characteristics, improved anodizing response and comparable corrosion resistance properties.

CAN 6061-T6 be annealed?

Answer: 6061-T6 aluminum is tempered and notorious for not bending easily. From a bending perspective, it’s always best to bend these parts in an annealed state and then temper them to the correct condition.

How is 6061-T6 made?

Alumina, or aluminum oxide, is extracted from the bauxite through a refining process using caustic soda and lime. Developed in 1935, 6061-T6 aluminum is a precipitation-hardened aluminum. Precipitation hardening uses high temperatures to increase the yield strength of aluminum.

How strong is 6061 T6 aluminum?

6061-T6. T6 temper 6061 has an ultimate tensile strength of at least 42,000 psi (290 MPa) and yield strength of at least 35,000 psi (241 MPa).

How strong is 6061-T6 aluminum?

What is the 6061-T6 aluminum tube pipe?

ASTM B241 6061 T6 aluminum tube 6061 aluminum pipe is a magnesium and silicon alloyed aluminum material . This good all-purpose alloy has good corrosion resistance and formability and has medium strength. It has good machining characteristics and has excellent appearance after anodizing.

What is the shear strength of aluminum 6061?

The shear strength of 6061 aluminum alloy is 207 MPa (30000 psi), and these values are summarized in Table 1. Fatigue strength is the ability of a material to resist breaking under cyclical loading, where a small load is repeatedly imparted on the material over time.

What is the 6061 aluminum flat bar?

Also known as 6061 aluminum flat bar, 6061 aluminum rectangular bar is an extruded solid aluminum bar that is versatile, easy to work with, and has a wide range of application uses. Aluminum rectangular bar 6061 is made from one of the most widely used heat treatable aluminum alloys in the industry. This alloy type is widely used for all types of fabrication projects where a lighter weight is needed, and corrosion resistance is a concern.

What is the 6061 aluminium alloy plate?

Alloy 6061 aluminum plates are one of the most versatile and widely used of the heat treatable alloys. This wrought tooling plate exhibits excellent machinability, weldability, and medium strength. Though less strong then most of the 2xxx and 7xxx alloys, 6061 is typically selected where welding or brazing is required or for its high corrosion resistance in all tempers.